Fluorolon PTFE 1034 is reinforced with carbon-graphite the percentage varying between 5
and 30%. The added fiber improves the wear properties, reduces extrusion. The coefficient of friction is slightly increased and for this reason, graphite is sometimes added to
compensate this side effect. The material has the ability to run under dry or wet conditions making it an ideal bearing and seal material.
and 30%. The added fiber improves the wear properties, reduces extrusion. The coefficient of friction is slightly increased and for this reason, graphite is sometimes added to
compensate this side effect. The material has the ability to run under dry or wet conditions making it an ideal bearing and seal material.
APPLICATIONS:
Fluorolon 1034 is used primarily for seals, seats, bearings, and insulators.
MECHANICAL PROPERTIES:
Property
Specified
Units
Method
Specific Gravity
2.06
gr/cc
ASTM-D792
Tensile Strength
2300
psi
ASTM-D1708
Elongation
105%
%
ASTM-D1708
Deformation
12.6
%
ASTM-D 621-59
Flexural Strength
4300
psi
ASTM-D790
Flexural Modulus
240,000
psi
ASTM-D790
Compressive Strength
2500
psi
ASTM-D695
Hardness
86
shore D
Coefficient of Thermal Expansion
47 10 x6th
in/in/deg.F
ASTM-D696
Water Absorption (24 hrs)
.007
%
ASTM-D570
Max. Service Temperature
500
F
–
Coefficient of Friction
.08
Static
M-D3702
This information corresponds to our current information on the subject. It is offered solely to provide suggestions for your own experimentation. It is not intended, however, to
substitute for any testing you may need to conduct to determine for yourself the suitability
of our products for your particular purposes. Since we cannot anticipate all variations in
actual end-use conditions, Advanced EMC Technologies makes no warranties and assumes
no liability in connection with any use of this information.